mould steel S136 AISI420 DIN1.2083 GB4Cr13

  • S136 steel bar - Dongguan songshun mould steel CO.,LTD.

    S136 steel Quick Details. Grade: Plastic mould steel; Standard: AISI, ASTM, BS, DIN, GB, JIS; Thickness: Max:800mm; Width: 205-810mm; Length: 2000-4000mm; Place of Origin: Guangdong, China (Mainland); Brand Name: Songshun; Model Number:GB4Cr13/AISI420/DIN1.2083/JISSUS420J2; Application: Mould steel

  • S136 Mould Steel - Detect-metals

    Detect Metals is the most acclaimed manufacturer, exporter, distributor and supplier of industrial S136 / DIN1.2083 Stainless Steel Round Bar For PVC Mould with required test certificates. Our material is certified to the Grade: S136 / AISI 420 / DIN 1.2083 / GB 4Cr13, Hardness: ≤ 229HBS Or 32~36HRC. Hot Rolled

  • Steel grades | The Tool Hub

    Jan 30, 2016 STAVAX S136, 420, ESR, Through hardened, 50-52, High purity, high polishability to mirror finish, with good corrosion resistance and low distortion after heat treatment. High quality mold inserts with mirror surface finish and good corrosion resistance, anti-corrosive cooling channel, best suitable for

  • SUS 420J2 S136 X40Cr14 DIN1.2083 420 Stainless Tool Steel

    HEAT TREATMENT. Forging: P20 plastic mould steel are forged at 1093°C (2000°F) down to 899°C (1650°F). Forging below 871°C (1600°F) is not recommended for these steels. Annealing: For maximum softness, heat uniformly to 1500 – 1650°F (816 – 899°C) and cool slowly in the furnace. Stress Relieving: Heat at 300

  • Choosing the optimum mould steel | The Tool Hub

    Nov 15, 2014 pre-hardened mould and holder steel • through-hardening mould steel • corrosion resistant mould steel. For corrosive resins such as PVC, UPVC, POM, The Tool Hub suggests using corrosion resistant steels such as: 2083 2083 ESR NAK80 420. 420SS ASSAB S136 ASSAB S136H 2316 etc. For abrasive

  • S136 / DIN1.2083 Stainless Steel Round Bar in all sizes, offer SS

    S136 / DIN1.2083 Stainless Steel Round Bar For PVC Mould. S136 / AISI 420 / DIN 1.2083 / GB 4Cr13; Hot rolled or forged condition, annealing or Pre-harden, black or machined surface; Hardness: ≤ 229HBS or 32~36HRC; Hot rolled technology: EAF+LF+VD; Forged technology: EAF+LF+VD+ESR+Forging +Q T +